ANALISIS SIFAT MEKANIK MATERIAL KOMPOSIT BERPENGUAT SERAT KARBON
Keywords:
Tensile; Young's Modulus; Composite; Carbon Fiber.Abstract
This research aims to determine the tensile, Young's modulus and shear modulus values through tensile testing using carbon fiber composite materials. In the tensile test, it was found that the tensile value increased in each variation, namely in the 3 layer and 5 layer variations with a percentage of 18.71% in the 3 layer variation and 48.51% in the 5 layer variation. The Young's Modulus value decreased with each variation, namely the 3 layer variation experienced a percentage decrease of 35.01% and the 5 layer variation experienced a percentage decrease of 9.2%.
References
Azas, S. (2017). Analisa Kekuatan Tarik Dan Geser Pada Bahan Komposit Yang Diperkuat Dengan
Serat Tumbuh tumbuhan (Doctoral dissertation).
Budiyono, S. (2011). Rancangan Alat Uji Geser pada Bahan Komposit Serat Alam dengan Memperhatikan Aspek Keterulangan Hasil Pengujian.
Hatta, I. (2016). Pengaruh Arah Serat Komposit Terhadap Kekuatan Geser “Carbon Fiber Reinforced Plastic (CFRP)” Berdasarkan Model IOSIPESCU. In Seminar Nasional IPTEK Penerbangan dan Antariksa XX-2016.
https://chatgpt.com/share/269ea2b3-8aad-4830-97a7-f97f062d8bdd
Widi, K. A., Pohan, G., & Sujana, W. (2020). Analisa Uji Balistik Produk Body Armor Material Komposit Poliester Berpenguat Serat Karbon , Rami dan Kapas. (Prosiding Seminar Nasional Teknik, 2020), 2020(Senastika), 5.
Wulandari, F., Komang, I., Widi, A., & Febritasari, R. (2022). 2 nd I Komang Astana Widi, 3 rd Rosadila Febritasari, 2022 Analisa Sifat Mekanis Pada Material Serat Karbon Dan Resin Epoxy Dengan Variasi Laminasi.